Cerium Based Metal-Organic Frameworks as an Efficient Separator Coating Catalyzing the Conversion of Polysulfides for High Performance Lithium-Sulfur Batteries.
Hong XJ, Song CL, Yang Y, Tan HC, Li GH, Cai YP, Wang H.
Hong XJ, et al.
ACS Nano. 2019 Feb 26;13(2):1923-1931. doi: 10.1021/acsnano.8b08155. Epub 2019 Feb 18.
ACS Nano. 2019.
PMID: 30763073
At the sulfur loading of 2.5 mg/cm(2), initial specific capacity of 1021.8 mAh/g at 1C was achieved in the Li-S cell with the Ce-MOF-2/CNT coated separator, which was slowly reduced to 838.8 mAh/g after 800 cycles with a decay rate of only 0.022% and the Coul …
At the sulfur loading of 2.5 mg/cm(2), initial specific capacity of 1021.8 mAh/g at 1C was achieved in the Li-S cell with the …