Cellulose nanofibers (CNFs) nanocomposites were prepared using poly(methylmethacrylate-co-methacrylic acid) (PMMA-co-MAA) to investigate the macromolecular mobility within the composite, with particular focus on the effect of H-bonding. Dynamic mechanical analysis (DMA) and broadband dielectric spectroscopy (BDS) were used to fully characterize the molecular mobility for which the effect of the introduction of H-bond forming moieties and the addition of CNFs (5 and 15 wt%) were assessed. Despite similar Tg values (determined by Differential Scanning Calorimetry), a deeper analysis of the relaxation times associated with the α-relaxation evidenced a significant effect induced by CNFs, which is in fact slowing down the macromolecular relaxation processes. The activation energy of the β-relaxation remained unchanged despite the introduction of MAA units in the main chain and the successive addition of CNFs. However, the latter led to the appearance at low frequencies of a new β'-relaxation correlated with the interactions between the CNF surface -OH groups and the -COOH groups of the matrix. The γ-relaxation showed a 45 % increase in activation energy from PMMA to PMMA-co-MAA + CNF nanocomposites regardless of the CNF content, due to the possibility of CNFs to interact and hinder the motion of the main chain methyl groups in α position.
Keywords: Cellulose nanofibers; Dielectric spectroscopy; Dynamic mechanical analysis; Methacrylate copolymer; Nanocomposites.
Copyright © 2024. Published by Elsevier Ltd.