We leveraged the potential of high χ-low N block copolymer (BCP), namely, poly[2-(perfluorobutyl) ethyl methacrylate]-block-poly(2-vinylpyridine) (P2PFBEMA-b-P2VP), and demonstrated its utility in next-generation nanomanufacturing. By combining molecular dynamics simulations with experiments, the χ value was calculated to be as high as 0.4 (at 150 °C), surpassing similar structures. Highly ordered features suitable for application were observed, ranging in periods from 19.0 nm down to 12.1 nm, with feature sizes as small as 6 nm. Transmission electron microscopy images of the BCP solutions indicated that preformed micelles in the solution facilitated the self-assembly process of the thin film. In addition, the vertical or parallel orientation of the cylindrical structure was determined by manipulating the solvent, substrate, and annealing conditions. Finally, guided by a wide topographical template, nearly defect-free directed self-assembly (DSA) lines with a resolution of 8 nm were achieved, highlighting its potential practical application in DSA lithography technology.
Keywords: advanced lithography; directed self-assembly; fluorine-containing; high χ block copolymer; orientation control.