This paper presents a comparison of six index properties collected during durability inspections of five Mexican seaports. Typical durability indicators such as compressive strength, saturated electrical resistivity, ultrasonic pulse velocity, percent total void content, capillary porosity, and chloride concentration profiles were analyzed to obtain empirical correlations with the non-steady-state chloride diffusion coefficient. These indices were compared to determine correlation coefficients that are the most important for obtaining better corrosion initiation forecasting. Two models of corrosion initiation time (ti) were used: Fick's second law of diffusion and the reported UNE-83994-2 (Spanish Association for Standardization, UNE) in which electrical resistivity was used to calculate concrete service life. The data from both models were cleaned using correlated variables, and the initial variables were compared with ti. The main result achieved was the verification of the feasibility of using correlations of variables to clean unnecessary data in order to calculate ti. Additionally, electrical resistivity was identified as one of the main durability indexes for in-service concrete structures exposed to marine environments. This is important because electrical resistivity is a non-destructive and reliable test that can be measured both in the laboratory and in the field very easily.
Keywords: data cleaning; electrical resistivity; reinforced concrete structures; service life.