Objective: To evaluate the effect of circular polarization (CP) and elliptical polarization (EP) of the B1 field on metal implant-induced artifacts of titanium (Ti) and cobalt-chromium (CoCr) hip arthroplasty implants at 1.5-T and 3.0-T field strengths.
Material and methods: In vitro Ti and CoCr total hip arthroplasty implants were evaluated using high transmit and receive bandwidth turbo spin echo (HBW-TSE) and slice encoding for metal artifact correction (SEMAC) metal artifact reduction techniques. Each technique was implemented at 1.5-T, which only allows for CP of B1 field as the system default, as well as 3.0-T, which permitted CP and EP. Manual segmentation quantified the size of the metal artifacts at the level of the acetabular cup, femoral neck, and femoral shaft.
Results: In the acetabular cup and femoral neck, 1.5-T CP achieved smaller artifact sizes than 3.0-T CP (28-29% on HBW-TSE, p = 0.002-0.005; 17-34% on SEMAC, p = 0.019-0.102) and 3.0-T EP (25-28% on HBW-TSE, p = 0.010-0.011; 14-36% on SEMAC, p = 0.058-0.135) techniques. In the femoral stem region, 3.0-T EP achieved more efficient artifact suppression than 3.0-T CP (HBW-TSE 44-45%, p < 0.001-0.022; SEMAC 76-104%, p < 0.001-0.022) and 1.5-T CP (HBW-TSE 76-96%, p < 0.001-0.003; SEMAC 138-173%, p = 0.003-0.005) techniques.
Conclusion: Despite slightly superior metal reduction ability of the 1.5-T in the region of the acetabular cup and prosthesis neck, 3.0-T MRI of hip arthroplasty implants using elliptically polarized RF pulses may overall be more effective in reducing metal artifacts than the current standard 1.5-T MRI techniques, which by default implements circularly polarized RF pulses.
Keywords: 3.0-T; Hip arthroplasty; MRI; Metal artifact; Polarization; Radiofrequency pulse.