High-Performance UV-Vis Photodetectors Based on a Lead-Free Hybrid Perovskite Crystal (MV)[SbI3Cl2]

Yunlin Lei; Shouyu Wang; Jie Xing; Hong Xu; Jing Han; Weifang Liu

doi:10.1021/acs.inorgchem.9b03277

High-Performance UV-Vis Photodetectors Based on a Lead-Free Hybrid Perovskite Crystal (MV)[SbI₃Cl₂]

Inorg Chem. 2020 Apr 6;59(7):4349-4356. doi: 10.1021/acs.inorgchem.9b03277. Epub 2020 Mar 25.

Authors

Yunlin Lei¹, Shouyu Wang¹, Jie Xing², Hong Xu², Jing Han¹, Weifang Liu³

Affiliations

¹ College of Physics and Materials Science, Tianjin Normal University, Tianjin 300387, China.
² School of Sciences, China University of Geosciences, Beijing 100083, China.
³ Tianjin Key Laboratory of Low-Dimensional Materials, Physics and Preparing Technology, Faculty of Science, Tianjin University, Tianjin 300072, China.

PMID: 32208647
DOI: 10.1021/acs.inorgchem.9b03277

Abstract

Low-dimensional lead-free organic-inorganic hybrid perovskites have gained increasing attention as having low toxicity, ease of processing, and good optoelectronic properties. Seeking for lead-free and narrow band gap organic-inorganic hybrid perovskites are of great importance for the development and application of photoelectric materials. Here, we reported a Sb-based organic-inorganic hybrid perovskite (MV)[SbI₃Cl₂], which has one-dimensional inorganic frameworks of the I-sharing double octahedra. (MV)[SbI₃Cl₂] shows a narrow direct band gap of 1.5 eV, and displays obvious photoresponse for the 532 nm light with rapid response speed of t_rise = 0.69 s, t_decay = 0.28 s. With an illumination power of 5 mW and a 50 V bias, the responsivities (R) and external quantum efficiency (EQE) for (MV)[SbI₃Cl₂] photodetector under 532 nm laser are 29.75 mA/W and 6.69% respectively. This Sb-based halide double perovskite material will provide an alternative material for photodetector devices.