Background: Different interbody grafts have been employed and evaluated for spinal fusion surgery. The Memory Metal Minimal Access Cage (MAC) is a hollow horseshoe shaped interbody fusion concept which provides a potentially major advantage with their small cage contact area and large graft space in comparison with other vertical cages.
Methods: This Biomechanical Cadaveric Study evaluates the primary stability and the amount of acute subsidence occurring in two new MAC cage designs; the Niti-l and Niti-s. Both cages were made of nitinol in the form of a wedge-shaped horseshoe with spikes on the edges. Differences were the higher weight and larger tranverse section area of the Niti-l due to his specific design with two different layers of thickness. Biomechanical axial compression tests were performed on ten fresh-frozen T11-L5 vertebral bodies.
Results: A direct relation between force at failure and BMD was found (p < 0.001). The displacements in the vertebral body at an axial force of 800 N were 1.91 mm and 1.88 mm for the NiTi-l and NiTi-s cage, respectively. The mean failure load for the NiTi-l cages was 2043 N, and 1866 N for de NiTi-s cages. No significant difference was established between the two cages.
Conclusion: The biomechanical strength of both NiTi-l and NiTi-s cages is good and comparable to each other with a limited amount of short-term subsidence after the initial implantation of the cage spikes into the bone.
Keywords: Cages; Interbody fusion; Memory metal minimal access cage; Nitinol; Spinal fusion.