Methylammonium lead halide perovskite has emerged as a new class of low-temperature-processed high-performance semiconductors for optoelectronics, but with photoresponse limited to the UV-visible region and low environmental stability. Herein, we report a flexible planar photodetector based on MAPbI3 microarrays integrated with NaYF4:Yb/Er upconversion nanoparticles (UCns) that offers promise for future high performance and long-term environmental stability. The promise derives from the confluence of several factors, including significantly enhanced photons absorption in the visible spectrum, efficient energy transition in the near-infrared (NIR) region, and inhibition of water attack by the hydrophobic UCns capping layer. The UCns layer aided in remarkably enhanced photodetection capability in the visible spectrum with detectivity (D*) reaching 5.9 × 1012 Jones, among the highest reported values, due to the increased photocarrier lifetime and decreased reflectivity. Excellent NIR photoresponse with spectral responsivity (R) and D* as high as 0.27 A W-1 and 0.76 × 1012 Jones were obtained at 980 nm, respectively, superior to the reported values of state-of-the-art organic-perovskite NIR photodetectors. Moreover, the hydrophobic UCns capping layer serving as a moisture inhibitor allowed significantly enhanced long-term environmental stability, e.g., 70% vs 27% performance retained after 1000 h exposure in 30-40% RH humidity air without encapsulation for the bilayer and the neat MAPbI3 devices, respectively. These results suggest that the composite based on perovskite and UCns is promising for constructing high-performance broadband optoelectronic devices with long-term stability.
Keywords: broadband photoresponse; long-term stability; perovskite; photodetector; upconversion nanoparticles.