Ferroelectric resistive switching (RS), manifested as a switchable ferroelectric diode effect, was observed in well-ordered and high-density nanocapacitor arrays based on continuous BiFeO3 (BFO) ultrathin films and isolated Pt nanonelectrodes. The thickness of BFO films and the lateral dimension of Pt electrodes were aggressively scaled down to <10 nm and ∼60 nm, respectively, representing an ultrahigh ferroelectric memory density of ∼100 Gbit/inch(2). Moreover, the RS behavior in those nanocapacitors showed a large ON/OFF ratio (above 10(3)) and a long retention time of over 6,000 s. Our results not only demonstrate for the first time that the switchable ferroelectric diode effect could be realized in BFO films down to <10 nm in thickness, but also suggest the great potentials of those nanocapacitors for applications in high-density data storage.
Keywords: BiFeO3; Schottky emission; high-density memory; nanocapacitor array; resistive switching; ultrathin film.